SECULIN® is a durable, cross-laminated LDPE film offering exceptional strength and tear resistance. Its high tensile strength, waterproofing, UV protection, and chemical resistance make it ideal for tough applications. Lightweight and flexible, SECULIN® ensures long-lasting performance in demanding environments, providing superior protection for various uses.
SECULIN® is crafted from a specially engineered Multilayer Multiaxis Oriented Cross laminated Film. Its unique composition offers exceptional puncture resistance and barrier properties, providing reliable protection for your assets in various environments.
SECULIN® is incredibly lightweight yet remarkably strong, offering superior protection compared to traditional films. Its puncture-resistant and crack-resistant properties ensure long-lasting durability, even in demanding conditions.
Unlike conventional films that may peel off, shred, or cause leaks easily, SECULIN® maintains its integrity, providing an effective barrier against moisture, dust, and other environmental elements.
SECULIN® boasts high UV properties, delivering enhanced crack and weather resistance. It ensures your assets remain protected, even in harsh outdoor conditions.
It is necessary to ensure the safety of any precious item for transport, storage and in the course of operations regardless of the field of work. Many times, traditional materials fail to offer the desired level of durability and protection from harsh working conditions hence resulting in, among other things, damaged goods and wastage in operations.
Different industries such as industrial manufacturing, agriculture and the transport sector continue facing challenges when it comes to protecting their assets. Products are often subject to risks such as puncture, tearing, moisture, sunlight, and even chemicals. Conventional packaging, or covering solutions may not have the appropriate strength and appropriate service life, which may cause damage to the product and due to the increase in costs of operation.
SECULIN® is the cross-laminated multilayer LDPE film whose geometries suit the stringent needs of such industries. This technology enables enhanced strength, tear resistance and flexibility of the films enabling reliability even in extreme conditions. It also comes with the benefits of being waterproof, UV and chemical resistant, thus ensuring that it can be used for good performance purposes, irrespective of the structure used, whether it is used for wrapping machines, sheeting bags, growing crops, or transporting and storing goods.
From packaging delicate electronics to safeguarding industrial machinery, SECULIN® is the perfect choice for a wide range of applications. Its versatility and superior performance make it suitable for diverse industries, providing reliable protection for your valuable equipment, machinery, and materials.
| Sr. No. | Cisuse | Name of the Test | Method | Units | Specified Requirements | Value Obtained |
|---|---|---|---|---|---|---|
| 1 | 6.1 | Workmanship | IS 14611-2016 | – | The tarpaulins covers shall be uniform in colour texture and finish and shall be substantially free from pin hole and particles of foreign matter. There shall be no other visible defects, such as holes tears or blisters. The edges shall be free from nicks & cuts visible to unaided eye. | Satisfactory |
| 2 | 6.3 | Accelerated Ageing tes | IS 7016 (Pt.-8) 1975 | – | The sample shall show no apparent deterioration like softening, stiffening, tackiness, brittleness discoloration and degradation of physical properties. | The sample show no apparent deterioration like softening, stiffening, tackiness, brittleness discoloration and degradation of physical properties. |
| 3 | 6.8 Table-1 |
Tensile Strength (Before Ageing) a) Longitudinal Direction b) Transverse Direction |
IS: 13360 (Pt.-5/ Sec-1) | Kg/cm2 | Min. 250 Min. 200 |
478 324 |
| Elongation at break (Before Ageing) a) Longitudinal Direction b) Transverse Direction |
% | Min. 400 Min. 300 |
768 654 |
|||
| 4 | 6.8 Table-1 |
Tensile Strength (After Ageing) (At 70 10 C for 168 hrs) a) Longitudinal Direction b) Transverse Direction |
IS: 13360 (Pt.-5/ Sec-3) | Kg/cm2 | (Max.) 30% decrease from the original | 394 (17.57%) 267 (17.59%) |
| 5 | 6.8 Table-1 |
Tear Strength (Before Ageing) a) Longitudinal Direction b) Transverse Direction |
IS: 14611-2016 Annexure-F | gf | Min. 2080 Min. 1600 |
3904 1856 |
| 6 | 6.8 Table-1 |
Tear Strength (After Ageing) a) Longitudinal Direction b) Transverse Direction |
IS: 14611-2016 | (Max.) 30% decrease from the original | 2880 (26.23%) 1472 (20.69%) |
|
| 7 | 6.8 Table-1 |
Tear Strength (After 192 hrs UV exposure) a) Longitudinal Direction b) Transverse Direction |
IS: 13360 (Pt.-5/Sec-1) & IS: 13360 (Pt.-5/Sec-3) | Kg/cm2 | Should be Min. 50% of original value | 304 (63.60%) 238 (73.46%) |
| Elongation at break (Before Ageing) a) Longitudinal Direction b) Transverse Direction |
% | 570 (74.22%) 444 (67.89%) |
||||
| 8 | 6.4 | Water Proofness Test | IS: 7016 (Pt.-4) | – | Shall not allow water to percolate through or become wet on its outer surface | Sample does not allow water topercolate through become wet on its outer surface |
Contact us now to explore how our innovative solutions can safeguard your assets. Let’s elevate your packaging together!